Complex formation and stability of colloidal wood resin pitch suspensions with hemicellulose polymers

journal contribution
posted on 2023-05-18, 05:35 authored by Karen Stack, Lee, R, Richardson, D, Trevor LewisTrevor Lewis, Garnier, G

Pinus radiata on the stability of wood resin colloids under varying ionic strength conditions with the addition of calcium chloride. A photometric dispersion analyser was used to study the kinetics of aggregation under shear conditions. Addition of the wood polymers to an aqueous dispersion of wood resins was found to cause destabilisation of the wood extractive colloids in two stages, separated by an apparent stabilisation region. The behaviour observed is typical of aggregation due to polymer bridging at low polymer addition, followed by steric stabilisation of the colloids at medium polymer concentration and depletion flocculation at higher polymer additions and then finally depletion stabilisation. At 10 mM calcium ion concentration, destabilisation of the colloids occurred at low wood polymer addition, while at wood polymer concentrations above 50 mg/L restabilisation of the colloids occurred at this level of calcium. The wood polymers were found to be unable to stabilise the colloids at high calcium levels of 50 mM. At high calcium levels the wood polymers themselves were found to undergo aggregation. The stabilisation of the colloids was found to be affected by the way in which the colloids and wood polymer complexes are formed and allowed to reorganise with time./p>   

Adsorption isotherms for the adsorption of the wood polymers onto wood resin coated surfaces were determined. A low affinity Langmuir isotherm was obtained in the absence of electrolyte indicating that interaction between the wood polymers and the wood resin arises due to hydrogen bonding between the carboxylic acid groups despite the negative charge on both. The higher than expected loading capacity showed that the wood polymers adsorb as aggregates which extend from the surface and act to screen the negative charge of the wood resin colloids. In the presence of 10 mM CaCl2 the isotherm was found to be modelled by a Freundlich isotherm with a greater amount of wood polymer being adsorbed due to folding of the wood polymer and reduction in its volume.

History

Publication title

Colloids and Surfaces A: Physicochemical and Engineering Aspects

Volume

441

Pagination

101-108

ISSN

0927-7757

Department/School

School of Natural Sciences

Publisher

Elsevier Science Bv

Place of publication

Po Box 211, Amsterdam, Netherlands, 1000 Ae

Rights statement

Copyright 2013 Elsevier B.V.

Repository Status

  • Restricted

Socio-economic Objectives

Paper products and pulp

Usage metrics

    University Of Tasmania

    Exports

    RefWorks
    BibTeX
    Ref. manager
    Endnote
    DataCite
    NLM
    DC