Development of in situ soft colloidal probe atomic force microscopy for probing the adhesion between wood extractives and model surfaces
journal contributionposted on 2023-05-18, 19:35 authored by Tham, YY, Karen Stack, Richardson, DE, Molino, PJ, Higgins, MJ, Trevor LewisTrevor Lewis
A new method to attach colloidal particles in situ directly onto atomic force microscopy (AFM) cantilevers was developed and used as colloidal probes. In this method, cantilever surfaces were hydrophobically functionalised and the colloids adhered without glue in an aqueous environment. Experiments measuring the interaction forces between colloidal probes, composed of either wood extractives or a range of model compounds normally present in wood extractives, and glass, cellulose, and chromium surfaces were carried out. Wood extractive colloids exhibited the strongest adhesion to glass control surface (7.0 mN m−1), followed in decreasing order by triolein, abietic acid and oleic acid colloids (3.9 mN m−1, 2.2 mN m−1 and 1.2 mN m−1 respectively). Adhesion onto a cellulose surface was strongest for triolein colloids (8.1 mN m−1) followed by oleic acid colloids (6.1 mN m−1), while adhesion forces for abietic acid and wood extractives colloids were similar (4.9 mN m−1 and 4.3 mN m−1, respectively). When attached to a chromium surface adhesion forces of abietic acid and wood extractives were strongest and similar (3.6 mN m−1 and 3.9 mN m−1, respectively); the weakest interaction at this surface was recorded for oleic acid colloids (0.8 mN m−1). Similar adhesion forces for wood extractive colloids and abietic acid colloids (onto cellulose and chromium surfaces) reinforces the proposal that abietic acid occupies the outer layer of wood extractive colloids. The differences in the interaction between the colloids and the cellulose and chromium surface helps to explain the transfer of resin acid exclusively over triolein or oleic acid from a cellulose paper surface onto chromium plated printing cylinders.
Publication titleColloids and Surfaces A: Physicochemical and Engineering Aspects
Department/SchoolSchool of Natural Sciences
Place of publicationNetherlands
Rights statementCopyright 2016 Elsevier B.V.